| GS-738 |
P20 (Ni) |
Pre-hardened to HB290-330 |
Quality Pre-hardened, uniform hardness and easy cutting. |
High toughness and High degree of polish. |
| GS-738H |
P20 (Ni) |
Pre-hardened to HB330-370 |
Quality Pre-hardened, uniform hardness and easy cutting. |
High toughness and High degree of polish. |
| GS-2311 |
P20 |
Pre-hardened to HB280-325 |
Pre-hardened Plastic mold steel. |
Long-run production of high wear-resistance plastic mold. |
| GS-2312 |
P20(S) |
Pre-hardened to HB270-330 |
Easy cutting, suitable for mass rapid processing. |
Suitable for plastic mold & mould frames. |
| GS-638 |
P20 |
Pre-hardened to HB315-360 |
Good processing performance. |
Suitable for high quality large mould frames & mould frames. |
| GS-2711 |
P20 premium edition |
Pre-hardened to HB215-240 |
High hardness & High toughness |
Suitable for high hardness, high toughness & High degree of polish, especially large mould. |
| GS-2083 |
420 |
Pre-hardened to HB280-310 |
Increase the hardness to HRC52, Anti-acid & high quality polish. |
Suitable for Acid plastic & high quality polish of mould. |
| GS-2083H |
420 |
Pre-hardened to HB230 (Highest) |
Pre-hardened, Anti-acid & high quality polish. |
Suitable for Acid plastic & high quality polish of mould. |
| GS-2316A |
SUS 420 J2 |
Pre-hardened to HB265-310 |
Increase the hardness HRC47, and good corrosion resistance. |
Suitable for High-acid-plastic of mould with high quality finish, and high quality anti-acid of mould. |
| GS-2316 |
SUS 420 J2 |
Pre-hardened to HB265-310 |
Pre-hardened, and very good corrosion resistance. |
Suitable for High-acid-plastic of mould with high quality finish, and high quality anti-acid of mould. |
| GS-2316ESR |
SUS 420 J2
Electroslag remelting |
Pre-hardened to HB180-210 |
High purity steel, for high quality finish of mould, and very good corrosion resistance. |
Suitable for High-acid-plastic of mould with high quality finish, and high quality anti-acid of mould. |
| GS-2344 |
H13 H13 Electroslag remelting (Modified) |
Pre-hardened to HB180-220 |
High heat resistance, for die casting steel. |
For Aluminum or Zinc alloy die casting. |
GS-2311
SRPER |
H13 H13 Electroslag remelting (Modified) |
Pre-hardened to HB230 |
High toughness of a hot-work die steel, superior impact strength 300J. |
For Aluminum or Zinc alloy die casting. |
| GS-2510 |
01 |
Pre-hardened to HB230 |
Good hardenability & good wear resistance. |
For cold pressure, punching die, punch chip and cut sheet mode. |
| GS-2379 |
D2 |
Pre-hardened to HB255 |
Chromium copper high toughness. |
For cold extrusion molding, tensile modulus, stainless steel sheet, punch chip. |
| GS-2767 |
6E7
High toughness multi-functional steel |
Pre-hardened to HB262 (Highest) |
Excellent toughness punching capacity, can be hardened to HRC50-54. |
For cold stamping and cut sheet mode, punching metal materials can be more than 10mm. |
| GS-440C |
440C |
Pre-hardened to HB215 |
Good wear resistance and corrosion resistance,
hardness up to 56 HRC, after heat treatment. |
For wear resistance and Anti-acid performance of plastic mould, Ex: Injection molding of glass fiber, production line with the fixture, surface and size of electronic components for high quality modulus. |
 |
| MUP |
P20 |
Pre-hardened to HBV270-320 |
Good hardness, good wear resistance and good processing performance, suitable for electrical erosion processing. |
Long-run production of high-quality plastic mold. |
 |
Porcerax
¢ºPM-35 |
Special sintered powder steel |
Pre-hardened to HV350-400 |
High quality pre-hardened, breathable, excellent anti-acid and anti-rust, easy cutting, good interface processing. |
For plastic and die casting, in removing trapped gas, solution quality and efficiency question. |
Porcerax
¢ºPM-35 |
Special sintered powder steel |
Pre-hardened to HV400-450 |
 |
| Moldmax 30 |
|
Pre-hardened to HRC26-32 |
High strength beryllium copper, good thermal conductivity, reduce injection cycle time and better heat dissipation. |
For need rapid cooling of the mold core and inserts. |
| Moldmax 40 |
|
Pre-hardened to HRC34-42 |
 |
| HIT75 MOD. |
|
Pre-hardened to about HB180-230 |
Good thermal conductivity, reduce injection cycle time. |
For need rapid cooling of the mold core and inserts. |
 |
| C1100P |
JIS H3100 |
|
High purity, good conductivity properties, easy processing, low variability. |
Copper electrode |
|
| 6061-T6/651/6511 |
|
Aging treatment HB 95 |
High resistance to corrosion of aluminum alloy, excellent bonding characteristics and plating. |
Blow film, blow mold, ultrasonic welding head and mechanical parts. |
| 7075-T651 |
|
Aging treatment HB 150 |
High strength and good hardness of aluminum alloy. |
Ultrasonic welding head and mechanical parts. |
 |
CERTAL
7022-T651 |
AIZnMgCu0.5 |
Pre-hardened to HB290-340 |
High strength and good hardness of aluminum alloy, good processing performance. |
Plastic injection mold, blow film, heating plates, ultrasonic welding head and mechanical parts. |
 |
| WUYANG 2311 |
P20 |
Pre-hardened to about HB290-340 |
Pre-hardened Plastic mold steel. |
General application plastic mold steel. |
| WUYANG 718 |
P20(Ni) |
Pre-hardened to about HB290-340 |
Pre-hardened Plastic mold steel. |
General application plastic mold steel. |
 |
| S50C-S55C |
1050-1055 |
Pre-hardened to about HB170-220 |
Good processing performance and very easy cutting. |
For plastic mold with board and mechanical parts. |
 |
| MEK4 |
DIN.8523
(High wear-resistant plastic mold steel) |
Pre-hardened to HB370-400 |
Both high hardness and high toughness characteristics, good wear resistance, nitriding, surface hardness of up to 800HV. |
Require high hardness, high toughness and high wear resistance of the plastic mold, the life of the mold be extended after nitriding. |
| X13T6W(236H)
|
420 Modified Electroslag remelting
(premium edition) |
Pre-hardened to HB290-300 |
High purity, high degree of mirror, high quality polish, good wear resistance and excellent anti-acid and anti-rust better than AISI420. |
Demanding the mirror mode, suitable for injection molding medical parts, acid-plastic of PVC, PP, PE, PC, PMMA, and food industry machinery components. |
| X13T6W(236)
|
420 Modified Electroslag remelting
(premium edition) |
Normalizing to about HB 240 or less |
High purity, high degree of mirror, high quality polish; through a quench-and-temper, hardness up to 52HRC, and also enhance the polishing performance and corrosion resistance. |
Demanding the mirror mode, suitable for injection molding medical parts, acid-plastic of PVC, PP, PE, PC, PMMA, and food industry machinery components. |
| ADC3 |
H11 Modified |
Annealing to about HB 235 |
Material chemical composition and microstructure control through strict, stable and uniform quality; toughness excellent, excellent thermal fatigue resistance, high heat, good hardenability, reduce the heat treatment deformation. |
High demand and large for the aluminum alloy, magnesium alloy die-casting mold. |
| SMV3W 1MPAX718S |
H11 Electroslag remelting |
Annealing to about HB 235 |
Material chemical composition and microstructure control through strict, stable and uniform quality; material purity better than AISIH13 toughness, excellent resistance to thermal fatigue. |
High demand and small and medium for the aluminum alloy, zinc alloy die-casting mold; injection can be used as PA, POM, PS,PE,EP of plastic die. |
 |
| IMPAX 718S |
P20 Modified |
Pre-hardened to HB290-330 |
Pre-hardened uniform, about 1.0% nickel. |
High degree of polishing, and the high demand within the module, for PA, POM,PS,PE,PP,ABS plastic. |
| IMPAX 718H |
P20 Modified |
Pre-hardened to HB330-380 |
Pre-hardened uniform, about 1.0% nickel. |
High degree of polishing, and the high demand within the module, for PA, POM,PS,PE,PP,ABS plastic. |
STAVAXS 136 |
420 Electroslag remelting |
Annealing to about HB215 |
High purity, high degree of mirror, high quality polish, excellent anti-acid and anti-rust, reduce the heat treatment deformation. |
The mirror mode of high acidity, can be guaranteed not corroded cooling pipe, suitable for PVC, PP,EP, PC, EMMA of plastic, and food industry machinery components. |
| STAVAXS 136H |
420 Electroslag remelting |
Pre-hardened to HB290-330 |
High purity, high degree of mirror, high quality polish, excellent anti-acid and anti-rust, reduce the heat treatment deformation. |
The mirror mode of high acidity, can be guaranteed not corroded cooling pipe, suitable for PVC, PP,EP, PC, EMMA of plastic, and food industry machinery components. |
| OPTIMAX |
420
(Optical-grade mirror steel) |
Annealing to about HB 215 |
Extremely high purity and degree of mirror, excellent anti-acid and anti-rust, reduce the heat treatment deformation. |
High anti-acidic, especially for high requirements and injection optical mirror mode. |
| CORRAX S336
|
Special Aging steel |
Solution heat treatment to about 32HRC |
Excellent corrosion resistance, by a simple aging treatment, hardness can be increased to 50HRC, dimensional stability, good welding performance, good polishing performance. |
Highly corrosive plastic mold, medical and food industry, engineering components. |
| ELMAX |
Special powder wear-resistant stainless steel |
Annealing to about HB 240 |
High wear, high resistance to corrosion, high compressive strength, reduce the heat treatment deformation. |
High acid and high wear-resistant requirements of the plastic mold,
suitable for engineering plastic and add glass fiber / flame retardant plastic mold, high demand of electronic modules, food industry equipment and accessories. |
| RAMAX168 |
420 (Sulfur) |
Pre-hardened to HB & 30-360 |
Easy cutting, high anti-acidic. |
Long life and corrosion of the mold, required surface finish is not high, but to be corrosion-resistant and easy processing modules and fixtures, such as rubber molds. |
| ORVAR 8407 |
H13
Electroslag remelting (Modified) |
Annealing to about HB 185 |
Hot-work die steel, high toughness and good heat resistance. |
Metel die casting, extrusion die, under the cover mold die, PA, POM, PS, PE,EP plastic mold. |
| ARNE DF2 |
O1 |
Annealing to about HB 190 |
Micro-deformation of oil steel, wear resistant. |
Can be widely used in metal cold stamping, jewelry embossing die. |
| XW42 |
D2 |
Annealing to about HB 210 |
High wear resistance, after quenching to maintain a high surface hardness, compressive strength and dimensional stability. |
Cold extrusion die, hobbing plate screws, precision metal mould. |
| VANADIS10 |
Special ingredients powder steel |
Annealing to about HB2 30-310 |
Excellent toughness and wear resistance, good hardenability and welding, can be flame hardened to HRC56-60, up to 5mm thick hardened layer. |
Precision cutting silicon steel or cutting board. |
| CALMAX635 |
High wear resistance multi-functional mold steel |
Annealing to about HB 200 |
|
For resistance to adhesive wear, such as adding enhancer plastic mold, compaction molds. |
 |
| PX88 |
P20 Modified |
Pre-hardened to HB290-330 |
Designed to weld cracking low sensitivity of the alloy composition, significantly improve the welding performance. |
Long-term production general plastic mold steel, well-polished performance. |
| NAK55 |
P21 vulcanize vacuum remelting
(Modified) |
Pre-hardened to HB370-400 |
High hardness, easy cutting, good welding performance. |
High performance plastic mold, rubber mold. |
| NAK80 |
P21 vacuum remelting
(Modified) |
Pre-hardened to HB370-400 |
High hardness, excellent special effects mirror, EDM good, excellent welding performance. |
Pitting and polished performance mold. |
| S-Star |
SUS420J2
Electroslag remelting(Modified) |
Pre-hardened to HB300-330 |
Excellent corrosion and wear mirror feature. |
Precision plastic mold, high degree of mirror mold. |
| SUS420J2 |
SUS420J2
Electroslag remelting(Modified) |
Annealing to about HB 229 (Highest) |
Excellent corrosion and wear mirror feature. |
Precision plastic mold, high degree of mirror mold. |
| DH31-S |
SKD61(Modified) |
Annealing to HB 190 |
Good hardenability, excellent resistance to thermal fatigue cracking, good solution loss of heat. |
Aluminum, magnesium alloy die-casting mold, die casting parts, aluminum extrusion die. |
| GOA |
SKS3 (Modified) |
Annealing to about HB 217 |
Alloy tool steel has good hardenability and excellent wear resistance. |
For cold pressure, punching die, molding, punch chip and cut sheet mode. |
| DC11 |
SKD11 |
Annealing to about HB 255 |
Excellent wear-resistant high-chromium tool steel. |
For cold extrusion molding, tensile modulus, stainless steel sheet, die raw materials of high hardness. |
| DC53 |
SKD11(Modified) |
Annealing to about HB 255 |
High toughness of chromium steel,
after quenching and tempering, hardness is still up to 60 HRC, required after the heat treatment is particularly beneficial WEDM, reduce the cracking phenomenon. |
Punching die, cold work die, deep drawing die, punch-roll forming, punch chip. |
 |
| P20HH |
P20 Modified |
Pre-hardened to HB330-370 |
Specially formulated chemical composition,
add a good forging process and a good compression ratio, mechanical properties better than P20 steel. |
Require high hardness, gloss, and
wear resistance of the plastic mold, suitable for production of PA,POM,PS,ABS plastic mold. |
| P20LQ |
P20
(Optical-grade mirror steel) |
Pre-hardened to HB330-370 |
By dual vacuum refining (VAD+VAR), polished steel, rigid inclusion and
segregation greatly reduced,extremely beneficial for the polishing. |
For requirements surface finish to mirror stage, without injection acid-plastic of mold. |
| |
|
|
|
|